Exploring the influence of iron substitution in lithium rich layered oxides Li2Ru1-xFexO3: triggering the anionic redox reaction.
Journal of Materials Chemistry A
, 5
(27)
pp. 14387-14396.
10.1039/c7ta04194b.
Preview |
Text
1373203.pdf - Accepted Version Download (3MB) | Preview |
Abstract
Lithium rich layered materials are an interesting class of materials which exploit both anionic and cationic redox reactions to store energy upwards of 250 mA h g−1. This paper aims to understand the nature of the redox reactions taking place in these compounds. Li2RuO3 was used as the base compound, which is then compared with compounds generated by partially substituting Ru with Ti and Fe respectively. Electrochemical tests indicate that Fe substitution in the sample leads to an improvement in capacity, cycle life and reduction of potential decay. To elucidate the reason for this improvement in operando diffraction experiments were carried out, highlighting the formation of a secondary de-lithiated phase. The distortion of the pristine structure eventually induces frontier orbital reorganization leading to the oxygen redox reaction resulting in extra capacity. Local changes at Fe and Ru ions are recorded using in operando X-ray absorption spectroscopy (XAS). It was noted that while Ru undergoes a reversible redox reaction, Fe undergoes a significant irreversible change in its coordination environment during cycling. The changes in the coordination environment of oxygen and formation of O2n− type species were probed in situ using soft X-rays.
Type: | Article |
---|---|
Title: | Exploring the influence of iron substitution in lithium rich layered oxides Li2Ru1-xFexO3: triggering the anionic redox reaction |
Open access status: | An open access version is available from UCL Discovery |
DOI: | 10.1039/c7ta04194b |
Publisher version: | https://doi.org/10.1039/c7ta04194b |
Language: | English |
Additional information: | This version is the author accepted manuscript. For information on re-use, please refer to the publisher’s terms and conditions. |
Keywords: | Science & Technology, Physical Sciences, Technology, Chemistry, Physical, Energy & Fuels, Materials Science, Multidisciplinary, Chemistry, Materials Science, RAY-ABSORPTION-EDGE, HIGH-CAPACITY, ION BATTERIES, HIGH-POWER, ELECTROCHEMICAL PROPERTIES, CATHODE MATERIALS, POSITIVE-ELECTRODE, MANGANESE OXIDE, SPINEL PHASE, PERFORMANCE |
UCL classification: | UCL UCL > Provost and Vice Provost Offices > UCL BEAMS UCL > Provost and Vice Provost Offices > UCL BEAMS > Faculty of Engineering Science UCL > Provost and Vice Provost Offices > UCL BEAMS > Faculty of Engineering Science > Dept of Chemical Engineering |
URI: | https://discovery.ucl.ac.uk/id/eprint/10086093 |
Archive Staff Only
View Item |