Data for charts,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
2. Which of the following materials would you consider using to gap fill wooden objects? ,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Acrylic resin,Glass microballoons,Balsa wood,Paper pulp,A mixture of fillers,Hydroxypropyl cellulose,Waxes,Sawdust,Animal glue,Long fibre tissue,Acrylic resin emulsion,Methyl cellulose,Wood flour,Epoxy resin,Phenolic microballoons,Paper mache,Polyvinyl Butyral,Polyvinyl Acetate,Commercial wood fillers,Chalk/gypsum,Polyvinyl Acetate emulsion,Cork granules,Fumed silica,Starch paste,Urushi,Plaster,Ethyl hydroxyethyl cellulose,Clay powder,Cellulose nitrate,AJK / BJK dough,Silicone rubber,Linseed oil
75%,68%,59%,49%,46%,42%,42%,39%,38%,38%,37%,37%,35%,31%,29%,27%,25%,23%,23%,22%,20%,19%,19%,17%,10%,10%,8%,8%,7%,6%,5%,3%
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
3. Which of the following materials would you NOT consider using to gap fill wooden objects? ,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Linseed oil,Plaster,Silicone rubber,AJK / BJK dough,Epoxy resin,Urushi,Cellulose nitrate,Chalk/gypsum,Commercial wood fillers,Clay powder,Animal glue,Waxes,Starch paste,Cork granules,Sawdust,Paper mache,Polyvinyl Acetate emulsion,Wood flour,Fumed silica,Hydroxypropyl cellulose,Ethyl hydroxyethyl cellulose,Methyl cellulose,Polyvinyl Acetate,Polyvinyl Butyral,Acrylic resin,Acrylic resin emulsion,Phenolic microballoons,Paper pulp,Balsa wood,A mixture of fillers,Glass microballoons,Long fibre tissue
73%,69%,67%,57%,55%,52%,51%,47%,46%,42%,36%,32%,30%,30%,25%,24%,23%,19%,17%,16%,16%,15%,15%,15%,14%,14%,13%,12%,11%,9%,8%,5%
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
4. What properties do you consider to be important when deciding on materials for gap filling wooden objects?,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,
Retreatability,Low amount of shrinkage on curing,Ability to colour with pigment,Ability to be reshaped after curing,Ability to paint after curing,Similar reaction RH,High flexibility,Texture,No colour change on ageing,Low level of hardness,High adhesion to substrate on curing,Low adhesion to substrate on curing,High level of hardness,High tack when wet,Low tack when wet,Low flexibility,Dissimilar reaction RH,,,,,,,,,,,,,,,
84%,81%,78%,76%,76%,75%,66%,62%,49%,46%,27%,26%,17%,14%,13%,10%,9%,,,,,,,,,,,,,,,